Download PDF
CC BY-NC-ND 4.0 · Eur J Dent 2018; 12(04): 491-495
DOI: 10.4103/ejd.ejd_207_18
Original Article
Dental Investigation Society

The effect of resistance grooves on the fracture toughness of zirconia-based crowns from mono and cyclic loading

Tarek Q. Qasim
1   Department of Industrial Engineering, Faculty of Engineering, Jordan University of Science and Technology, Irbid, Jordan
,
Billal M. El-Masoud
2   Department of Prosthodontics, Jordan University of Science and Technology, Irbid, Jordan
,
Ahmed M. Abu Laban
2   Department of Prosthodontics, Jordan University of Science and Technology, Irbid, Jordan
› Author Affiliations
Further Information

Publication History

Publication Date:
23 September 2019 (online)

Also available at
   Permissions and Reprints

ABSTRACT

Objective: Prosthetic molar crowns in service are subjected to chewing loads, which cause a shift or dislodgment. The objective of this study is to investigate whether the addition of resistance grooves to the proximal surfaces of the abutment teeth would enhance the fracture resistance of the zirconia crowns and to compare between the patterns of cracks development on the zirconia crowns after the application of mono loading versus cyclic loading forces. Materials and Methods: Thirty-six all-ceramic zirconia cored crowns were prepared on the same abutment. Resistance grooves were added to the mesial and distal surfaces of 16 abutments. Before testing, all specimens subjected to thermal aging. Two groups of crowns were then subjected to cyclic axial and lateral forces for 1,250,000 cycles in aqueous conditions. Two groups of samples were also tested in monoloading fashion. Results: The crack pattern between mono and cyclic loading were compared. The crown fracture resistance was compared in the two types of abutments, with and without grooves. The results confirmed that the grooves addition had no effect on critical conditions to initiate failure in the case of mono loading. In cyclic loading, grooves addition increased the critical loads in the order of two. Failure patterns and location were obtained. Conclusions: The results showed that the location of retention grooves halted the failure in the surfaces where it was located in all loading mechanisms used in this study.

Key words:

All ceramic crowns - chewing simulator - failure modes - thermal aging
 

  • REFERENCES

  • 1 Sakaguchi RL, Powers JM. Craig's Restorative Dental Materials. 13th ed.. Elsevier/Mosby, Philadelphia, PA, USA: 2012
    Google Scholar
  • 2 Lawn BR, Bhowmick S, Bush M, Qasim T, Recow D, Zhang Y. Failure modes in ceramic-based layer structures: A basis for materials design of dental crowns. J Am Ceram Soc 2007; 90: 1671-83
    CrossrefGoogle Scholar
  • 3 Linhares LA, Pottmaier LF, Lopes GC. Fracture resistance of veneers in premolars. Eur J Dent 2018; 12: 191-8
    Article in Thieme ConnectPubMedGoogle Scholar
  • 4 Zhang Y, Chai H, Lee JJ, Lawn BR. Chipping resistance of graded zirconia ceramics for dental crowns. J Dent Res 2012; 91: 311-5
    Google Scholar
  • 5 Kim B, Zhang Y, Pines M, Thompson VP. Fracture of porcelain-veneered structures in fatigue. J Dent Res 2007; 86: 142-6
    Google Scholar
  • 6 Beuer F, Aggstaller H, Edelhoff D, Gernet W, Sorensen J. Marginal and internal fits of fixed dental prostheses zirconia retainers. Dent Mater 2009; 25: 94-102
    CrossrefPubMedGoogle Scholar
  • 7 Beuer F, Stimmelmayr M, Gernet W, Edelhoff D, Güh JF, Naumann M. et al. Prospective study of zirconia-based restorations: 3-year clinical results. Quintessence Int 2010; 41: 631-7
    PubMedGoogle Scholar
  • 8 Mukmin I, Qasim T, Hu XZ. Contact damage of curved zirconia/epoxy bi-layers. Strength Fract Complex 2007; 4: 213-23
    Google Scholar
  • 9 Donny PV. Zirconia abutments: Modern day implantology. Int J Oral Implantol Clin Res 2012; 3: 133-7
    Google Scholar
  • 10 Potts RG, Shillingburg Jr. HT, Duncanson Jr. MG. Retention and resistance of preparations for cast restorations 1980. J Prosthet Dent 2004; 92: 207-12
    CrossrefPubMedGoogle Scholar
  • 11 Parker MH, Gunderson RB, Gardner FM, Calverley MJ. Quantitative determination of taper adequate to provide resistance form: Concept of limiting taper. J Prosthet Dent 1988; 59: 281-8
    CrossrefPubMedGoogle Scholar
  • 12 Parker MH. Resistance form in tooth preparation. Dent Clin North Am 2004; 48 : v-vi, 387-96
    CrossrefPubMedGoogle Scholar
  • 13 Ozcan N, Sahin E. In vitro evaluation of the fracture strength of all-ceramic core materials on zirconium posts. Eur J Dent 2013; 7: 455-60
    Article in Thieme ConnectPubMedGoogle Scholar
  • 14 Kern M, Strub JR, Lü XY. Wear of composite resin veneering materials in a dual-axis chewing simulator. J Oral Rehabil 1999; 26: 372-8
    CrossrefPubMedGoogle Scholar
  • 15 Nilavarasan N, Hemalatha R, Vijayakumar R, Hariharan VS. Comparison of compressive strength among three different intracanal post materials in primary anterior teeth: An in vitro study. Eur J Dent 2016; 10: 464-8
    Article in Thieme ConnectPubMedGoogle Scholar
  • 16 Stawarczyk B, Ozcan M, Roos M, Trottmann A, Hämmerle CH. Fracture load and failure analysis of zirconia single crowns veneered with pressed and layered ceramics after chewing simulation. Dent Mater J 2011; 30: 554-62
    CrossrefPubMedGoogle Scholar
  • 17 Qasim T, Bush M, Hu XZ. The influence of complex surface geometry on contact damage in curved brittle coatings. Int J Mech Sci 2006; 48: 244-8
    CrossrefGoogle Scholar
  • 18 Qasim T, Ford C, Bush M, Hu XZ, Bongué-Boma M. Effect of coating thickness on crack initiation and propagation in non-planar bi-layers. Mater Sci Eng 2006; 419: 189-95
    CrossrefGoogle Scholar
  • 19 Qasim T, Bush MB, Hu X, Lawn BR. Contact damage in brittle coating layers: Influence of surface curvature. J Biomed Mater Res B Appl Biomater 2005; 73: 179-85
    Google Scholar
  • 20 Rudas M, Qasim T, Bush M, Lawn B. Failure of curved brittle layer systems from radial cracking in concentrated surface loading. J Mater Res 2005; 20: 2812-9
    CrossrefGoogle Scholar
  • 21 Whitton A, Qasim T, Ford C, Hu XZ, Bush M. The role of skirt geometry of dental crowns on the mechanics of failure: Experimental and numerical study. Med Eng Phys 2008; 30: 661-8
    CrossrefPubMedGoogle Scholar
  • 22 Barani A, Chai H, Lawn BR, Bush MB. Mechanics analysis of molar tooth splitting. Acta Biomater 2015; 15: 237-43
    CrossrefPubMedGoogle Scholar
  • 23 Lu PC, Wilson P. Effect of auxiliary grooves on molar crown preparations lacking resistance form: A laboratory study. J Prosthodont 2008; 17: 85-91
    CrossrefPubMedGoogle Scholar
  • 24 deJager N, deKler M, van der Zel JM. The influence of different core material on the FEA-determined stress distribution in dental crowns. Dent Mater 2006; 22: 234-42
    CrossrefPubMedGoogle Scholar